Thermoplastic material containing towel

ABSTRACT

A durable launderable towel has a thermobonded core of thermoplastic and other fibers. The towel has at least one cover sheet which is preferably formed with apertures and has a limited stretchability. Limited stretchability may be achieved by prestretching and heat setting the cover sheet prior to assembly into a towel. The towel is also densified in a field pattern and is typically densified at the peripheral edge. Embossing is preferably used to form these densified areas. The combination of thermobonding the core, embossing and the use of apertured cover sheets results in a towel having the softness, drape and feel approaching that of cloth. By controlling the embossing on the wiping surface of the towel, a towel with surfaces having different wipe dry characteristics and textures can be produced.

REFERENCE TO CO-PENDING APPLICATION

This is a continuation-in-part application of U.S. application Ser. No. 07/384,218 filed now U.S. Pat. No. 5,030,500, July 21, 1989 to Perdelwitz, Jr., et al. and entitled, "Thermoplastic Material Containing Towel."

BACKGROUND OF THE INVENTION

The present invention relates to absorbent towels which contain thermoplastic materials and more specifically to durable washable plural layer composite towels which include an absorbent layer formed from a mixture of thermoplastic and other nonthermoplastic fibers, such as wood pulp fibers.

BACKGROUND ART

Many prior art devices exist for wiping liquids, dirt, soil, grease, dust and the like from surfaces. These surface wiping devices can generally be referred to as towels.

Among the most common surface wiping devices are rags (scraps of woven fabrics) and cloth towels. Durable devices used in restaurants include terry and ribbed terry towels of varying sizes. These towels are woven textile fabric and are generally made from cotton or blends of cotton and synthetic fibers. Bar towels are typically of a woven textile sometimes referred to as "linen", but which are actually made from cotton or cotton blends. Although strong and absorbent, these products are relatively expensive. By their nature, these cloth towels generally leave the wiped surface wet; the residual water usually being present in the form of large drops which contribute to streaking and spotting. Durable cloth bar towels of this type have excellent feel and are laundered many times and reused. However, such towels may become so soiled with grease or other substances that laundering is unlikely to clean the towels and remove stains. In such a case, the towels are typically replaced with costly new towels.

In addition to cloth towels, disposable towels have also been used. Disposable, as used herein, refers to devices intended to be used at most a few times and then discarded. As such, the concept of a disposable product excludes the laundering of the device, although disposable products may be rinsed once or several times during their effective life and reused. Such rinsing is not to be considered to be laundering as used in connection with the concept of durable devices. In contrast, durable towels are suitable for laundering and reuse.

One type of disposable towel is described in U.S. Pat. No. 4,239,792 of Ludwa. The towels of this patent comprise a core sandwiched between outer surface wiping elements. The core is described as preferably being of a paper-based material, with a mass of nonwoven or woven fabric or foam materials also being mentioned as possibilities. Other core materials mentioned in this patent include bonded air felts formed from wood pulp fibers; single ply and multi-ply nonwoven or woven fabric; and absorbent cellulose, polyurethane, and polyester foams. The basis weight of the core is indicated to be from about sixteen to eighty grams per square meter. The outer surface wiping layers are each described as generally being of a single ply of nonwoven fabric, although sub-elements are also mentioned. Layers of bonded fibers or mechanically entangled fibers are mentioned, with the preferred material being one prepared by a process which tends to provide apertures within the fabric. Sontara®, a spun-laced nonwoven polyester product from Du Pont Corporation is one specifically mentioned material. The cover and core are laminated together with the patent stating that any conventional method of laminating can be used and specifically mentioning sewing and the use of latex adhesives.

Although relatively inexpensive in comparison to cloth towels, the wipes of the Ludwa patent are specifically described as disposable, which is defined to exclude laundering for reuse. Thus, these wipes lack desired durability for repeated launderings and reuse.

U.S. Pat. No. 4,469,734 of Minto, et al. describes microfiber web products made from meltblown microfibers. The webs are formed or provided with apertures by, for example, hot needling or by passing the web between differentially speeded rolls. The addition of fibers such as wood pulp to the web is mentioned. These webs are limited in strength and absorbency characteristics. However, one embossing pattern shown in this patent is similar to one specific exemplary embossing pattern utilized in towels of the present invention.

Finally, U.S. Pat. No. 4,886,697 of Perdelwitz, et al., entitled "Thermoplastic Material Containing Absorbent Pad or Other Article," issued Dec. 12, 1989, is incorporated by reference herein in its entirety. The Perdelwitz, et al. patent application describes the manufacture of absorbent articles, including laminated articles having cover sheets and a core formed of thermoplastic and other fibers. A number of suitable commercially available cover sheets are described, including Sontara®. The resulting laminated product can be embossed at field locations within the boundaries of the product and also can be densified at the edge margins. Example 12 of this patent relates specifically to a towel. Although extremely durable, the towel described in this example is distinguishable in drape and feel from cloth towels and has been found not to be launderable for at least five wash and dry cycles. Example 4 of this patent also describes the blending of relatively long polyester fibers with Pulpex® fibers and wood pulp fibers.

Therefore, although thermoplastic fibers have been combined with other fibers and used in the manufacture of articles, a need exists for improved towels of this type.

SUMMARY OF THE INVENTION

In accordance with one aspect of the present invention, a core or absorbent layer for a towel is formed of a mixture of fibers comprising at least one thermoplastic material and other fibers, such as wood pulp fibers. The core may be bonded together, as by thermobonding by heating the mixture to a temperature above the melting point of the fibers of at least one thermoplastic material in the mixture. Preferably the core is sandwiched between a pair of cover sheets of a liquid permeable material. Most preferably the cover sheets are of an apertured nonwoven material and the material is embossed with a pattern of embossing areas which, in combination with the apertured cover stock and core, results in a towel with a texture, hand and softness which approximates the feel of natural towels.

It has also been found that the launderability and durability of a towel of such material is enhanced by using cover sheets of a material with limited stretchability. More specifically, cover sheets of a material which stretches no more than about eighty percent in either the machine or cross machine directions, and most preferably a material which stretches no more than about sixty to seventy percent, result in a more durable towel. Although not to be limited to a particular theory, it is believed that stretching and contraction of towels of these types of materials during washing and drying cycles associated with laundering increases the fracturing and cracking of bonds between the core fibers forming such towels and contributes to the disintegration of the core during laundering. By using cover sheets of reduced stretchability, more durable towels result. One specific approach which may be used to provide cover sheets of this limited stretch characteristic is to prestretch and heat set such prestretched cover sheets prior to incorporation of these sheets in a towel.

The towel may be compressed and densified along its peripheral edge to provide a substantial liquid seal at the edge. The densified edge also adds to the durability of the towel.

The durability of towels of this type is also enhanced by the inclusion of some reinforcing fibers in the core of a sufficient length to span the distance between the embossed areas of the towel. These reinforcing fibers are selected so as to not be degraded during thermobonding of the towel so that they contribute to the tensile strength of the towel.

An important characteristic of the towel of the present invention is its durability. That is, such towels may be laundered under normal conditions a number of times for reuse. On average, the towels of the present invention are launderable at least about five times while still maintaining their integrity for use. For purposes of this application, a durable towel is defined as one which is launderable under normal conditions at least five times. Laundering under normal conditions refers to washing the towels with detergent, with our without bleach, in commercial or residential-type washing machines and drying these towels in a dryer, typically on low heat. This allows the towels to be cleaned for reuse. Yet, because the towels are of relatively inexpensive materials, in the event they become too soiled or stained for cleaning and, after their useful life, they may be simply replaced without incurring the high relative costs associated with conventional cloth towels.

Accordingly an object of the present invention is to provide improved thermoplastic material containing towels.

Another object of the present invention is to provide strong towels of such materials which are relatively strong and durable for laundering and reuse, yet are relatively inexpensive.

A further object of the present invention is to provide towels of such materials which have a hand, drape and feel which approximates cloth.

Still another object of the present invention is to provide such towels which minimize the leakage of liquids and dust from their edges.

A still further object of the present invention is to provide such towels which can be produced at a cost effective and high volume rate.

The present invention relates to the above features and objects individually as well as collectively.

These and other objects, features and advantages of the present invention will become apparent with reference to the following detailed description and drawings.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a schemat of one form of apparatus for manufacturing towels of the present invention;

FIG. 2 is a perspective view of a pair of embossing rolls which may be utilized in compressing and heat sealing the peripheral edges of towels made in accordance with the present invention;

FIG. 3 is a schematic illustration of one embodiment of an apparatus for cutting towels during manufacture thereof;

FIGS. 4a and 4b are plan views of the surface of one form of embossing roll used in manufacturing towels of the present invention; and

FIG. 5 is a perspective view of one form of a towel in accordance with the present invention with only a portion of the towel shown with the resulting surface texture.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENT General Description of Materials Thermoplastic Fiber Containing Core

For purpose of convenience, the thermoplastic fiber containing layer will be referred to herein as a core. However, it will be appreciated that in two layer laminated towels, the core itself respectively comprises one of the outer layers of the towel. Thus, in such a case the core would not be sandwiched between two or more cover layers. Also, the core itself may be laminated, thus being formed of sub-elements, as may the cover sheets.

As previously mentioned, the core is formed from a mixture of at least one thermoplastic material or material containing fiber in combination with one or more other types of fibers. The core forming fibers, on the average, have a length to diameter or cross sectional dimension ratios of greater than 5 and typically have ratios close to 100 or more.

Suitable thermoplastic fibers are typically made from thermoplastic polymers and are commercially available. These thermoplastic fibers have a high surface area to diameter ratio and are capable of melting when subjected to heat. Representative thermoplastic fibers are made from polyethylene, polypropylene, copolymers of ethylene and propylene, and copolymers of propylene and other 1-olefins such as 1-butene, 4-methyl-pentene-1, and 1-hexene. Grafted polyolefins pulps may also be used, in which maleic anhydride or styrene groups are grafted. In some embodiments, the thermoplastic fibers are composed solely of one type of thermoplastic. In other embodiments, the fibers are composed of mixtures of two or more types of thermoplastic fibers. Bicomponent fibers, such as comprised of polyethylene and polypropylene, may also be used. Polyester fibers are still another example of suitable fibers. Cellulose acetate is a further example of a suitable fiber. The thermoplastic fibers may also be fibers coated in whole or in part with thermoplastic materials.

Suitable commercially available products for making the thermoplastic fibers include Pulpex® E-338 from Hercules, Inc., a polyethylene based product; Kodel® from Eastman Kodak Corporation, a polyester based product; and Vinyon® from Celanese Corporation. However, Pulpex® is less preferred because it tends to melt at about 130° C., a temperature which may be exceeded in some dryers. In contrast, Kodel®is an amorphous polyester material which softens at about 170° C., but does not melt at such a temperature, and is therefore more suitable for use in a commercial dryer.

As explained in greater detail below, assume the thermoplastic materials are comprised of a mixture of more than one type of thermoplastic fibers, such as polyethylene and polyester fibers or polyester and high melt polyester fibers. In this case, during thermobonding, the core may be heated to a temperature sufficient to melt the lower melting point thermoplastio fibers without melting the higher melting point thermoplastic fibers. Consequently, the integrity of these latter fibers is preserved and strengthens the resulting core. In addition, by making the higher melting temperature fibers of a relatively long length, such as equal to or greater than about one-half inch, cores of enhanced tensile strength are produced. More specifically, it is desired that these higher melt temperature reinforcing fibers be long enough to span the distance between the embossing or other bond locations of the core so that they bridge the space between bond locations and contribute to the tensile strength of the towel in X, Y and Z directions. The Z direction refers to the direction which is perpendicular to the surfaces of the cover sheets. These reinforcing fibers also tend to reduce the shrinkage of the towels during laundering.

Preferably, for durable towels, the core has thermoplastic materials in an amount of from about 15%-40% by weight, and other fibers, such as wood pulp, make up the remainder of the mixture. However, greater or lesser percentages of thermoplastic materials may be used, although this affects the drape of this fabric.

As previously mentioned, the fibers mixed with the thermoplastic fibers to form the core may include wood pulp. These fibers are commercially available from a number of companies, including Weyerhaeuser Company, the assignee of the present application. In addition to wood pulp fibers, other nonthermoplastic synthetic and natural staple fibers such as rayon, cotton and the like may be included in the core forming mixture.

Also, depending upon the particular application, other absorbent materials may be added to the mixture. After the mixture is thermobonded or otherwise bonded, e.g. by adhesive, these added materials are substantially retained in place due to the bonding. The densified edge sections of the article also help retain these materials in place. Therefore, the tendency of these materials to escape or migrate from the article and into the external environment is reduced. Materials are selected which do not substantially degrade when subject to the temperature conditions that are present during thermobonding. Also by selecting thermoplastic materials with relatively melting points, thermobonding can be accomplished at a temperature which minimizes the possible thermal degradation of these materials. However, materials are selected so as not to melt when the towel is dried in a dryer. Among the suitable materials that may be included in the mixture are absorbent materials such as desiccants and superabsorbent materials. In practice, any absorbent or adsorptive material can be added to the mixture. Representative examples include activated carbon, acid clay, active alumina, diatomaceous earth, silica gels and the like. Relatively newly developed superabsorbent polymers, such as cross-linked polyacrylate commercially available under the brand name "Drytech" from Dow Chemical Company may also be included. Other absorbent substances generally used in the form of a powder can conveniently be fixed in the core during bonding.

In addition, oil absorbent materials such as polymers, including polynorbornene, available under the brand name "Norsorex" from C.d.F. Chemie of France, may be included. In addition, deodorizing materials such as odor absorbing, odor masking, odor inhibiting and odor eliminating materials, may be included in the core forming mixture. Examples include baking soda, cedar oil and other fragrances. Dyes or other colorants may also be added to the core. Again, the bonding of the core helps fix these materials in place.

Instead of including these absorbent materials in the core forming mixture prior to bonding, they may be placed on one or both surfaces of the core following the core formation. These materials may be included in an adhesive coating on the core or simply sprayed on the core in liquid form and allowed to dry.

Finally, due to the methods of forming a core and articles of the present invention, cores of widely varying basis weights may be manufactured. For durable towels with a textile-like drape, core basis weights of from about 50 to 150 g/m² are preferred with a basis weight of about 80 g/m² being most preferred.

Cover Laver Materials

The facing or covering layers typically comprise a preformed sheet or web and may be of a nonwoven thermoplastic containing material. These cover layers may be dyed or otherwise colored if desired. During manufacture, the core forming mixture is typically deposited on the bottom one of the covering sheets to the desired depth. To prevent melting of the covering sheet during thermobonding, the cover sheets are selected to have a melting point which is higher than the melting point of the thermoplastic fibers of the core which are to be melted during thermobonding. When the covering sheet and deposited mixture pass through the thermobonder, the core fibers are thermobonded together and to the facing sheet. The top facing or covering sheet may also be passed through the thermobonder. Also, the top covering sheet, or both top and bottom covering sheets, may be secured to the core following the thermobonding of the core.

Thus, the selection of the covering sheet material will depend at least in part upon the thermoplastic fibers included in the core and the manufacturing approach. Representative covering sheet materials include thermoplastic coated materials such as rayon which is resin or otherwise coated with a thermoplastic layer, polyolefin materials, spun laced materials such as polyester, rayon, acrylic, cotton, polypropylene and other spun laced materials, resin bonded polyester and polypropylene, spun bonded polyester and polypropylene, thermobonded polyester and polypropylene, carded polyester and polypropylene, melt blown polypropylene, polyethylene films of varying densities, polypropylene films, apertured films and other suitable materials apparent to those skilled in the arts.

In addition, if a manufacturing method is employed wherein heated air is pulled through the core and the facing sheet during thermobonding, the facing sheet must be perforated or otherwise breathable.

Some commercially available suitable nonwoven continuous filament products include Cerex®, a nylon material from James River Corporation, Reemay®, a spun bonded polyester material from Intertec Corporation, Sontara®, a spun laced polyester product from Du Pont Corporation, and Chicopee wipe, a spun-laced polyester product from Chicopee Company.

Again, a wide variety of facing sheet materials may be used. These facing sheets are thermoplastic or thermoplastic containing for those applications in which the facing sheet is to be thermobonded to the core. If the facing sheets are secured to the core in another manner, such as by adhesive, then they need not be thermoplastic. Nonwoven materials are exemplary facing sheets because such materials readily allow the passage of liquids to the absorbent core.

Although variable, the most preferred facing or covering sheets for towels have a basis weight of from about 20 to 80 g/m² and are liquid permeable to permit the passage of liquid to the core. Furthermore, covering sheets of the type prepared by a process which produces apertures in the fabric are especially preferred. When embossed as explained below, these apertured cover stock materials, such as Sontara® and Chicopee wipe, produce an inexpensive towel which has the drape, softness and feel approximating that of bar towels and other textile fabrics.

Apertured cover stocks preferably have holes which are no more than about three millimeters in diameter so as to still contain the core fibers therein. Also, during thermobonding, some of the thermoplastic material melted during this process flows into these apertures to enhance the bonding of the cover stock to the core. In addition, some of the pulp or other fibers in the core tend to strike or extend into and in some cases through these apertures to a limited extent degree so as to provide a path for the flow of liquid to the core.

To provide a durable towel, that is one that will survive on average at least five launderings under normal conditions, cover sheets of material with limited stretchability are preferred. More specifically, it is preferred to utilize cover layers of a material which stretches no more than about eighty percent in either the cross machine or machine directions and more preferably, no more than about sixty to seventy percent in either direction. Typically, the cross machine direction stretch is of more concern because during manufacture of nonwoven materials the machine direction stretch is often limited by the manufacturing approach used for these materials. One specific approach for achieving covering layers of the desired relatively low stretchability is to prestretch the covering layers and heat set the covering layers in their prestretched condition to thereby limit the stretchability of these layers when subsequently incorporated into a towel. As a specific example, assuming that Sontara® is the desired covering material, this material may be stretched about forty-five percent and heated to about 200° C. and thereafter cooled to set the fabric in this prestretched condition. With Sontara® there is no need to prestretch and set the sheet in the machine direction because the stretchabilr.ty of this material in the machine direction is already within the desired upper limit.

As previously mentioned, it is believed that washing and drying of a thermobonded towel causes the stretching of the towel during washing followed by contraction of the towel during drying. Repeated stretching and contraction causes some fracturing of the towel, meaning the core of the towel starts to separate and form pills. By limiting the stretchability of the covering layers, less stretching and contraction occurs during the laundering cycle. Consequently, the towel survives a greater number of laundering cycles prior to disintegration. This will become more apparent in connection with the examples discussed below.

In addition, when cover sheets of nonwoven materials are used, the grab tensile strength of these materials in both the machine and cross machine directions is preferably greater than or equal to three kilograms. Grab tensile strength is determined by positioning one edge of a 4"×6" sample of material in a clamp and then pulling on the opposite edge of the material until failure occurs. With grab tensile strengths being greater than or equal to three kilograms, the cover sheet materials tend to hold up during the abuses associated with laundering and drying of the towels.

Manufacturing Method

In one typical approach, the thermoplastic and other fibers to be used in forming the core are blended by any of the known blending methods. Optional absorbent and other additives may also be blended in at this time. Such methods include the preparation of a pulp sheet by a conventional paper-making procedures or by conventional dry blending methods. The resulting sheet is then rolled up to form a roll of core forming fibers such as indicated at 10 in FIG. 1. A sheet 12 is fed from roll 10 to a fluff preparation zone 14. At zone 14, the web 12 is formed into a fluff pad by conventional methods such as hammermilling or air forming.

In other suitable approaches, the thermoplastic core forming fibers may be fluffed separately from the other fibers, deposited in a hopper 16, and distributed by an air stream into the fluff preparation zone. In this case, the wood pulp and other fibers are similarly fluffed and deposited in a hopper 18 and distributed by an air stream within the fluff preparation zone for mixing with the thermoplastic fibers from the hopper 16. Absorbent material additives may also be added to hoppers 16 and 18. Vacuum air laying techniques may also be employed. Similarly, pulp sheets can be passed through a hammermill with the thermoplastic fibers being added in a separate step. Thus, the specific manner of forming the mixture of thermoplastic and other fibers that eventually become the core of the article is not critical.

In the illustrated approach, a thermoplastic containing face sheet, such as a breathable, nonwoven, liquid permeable apertured facing sheet web 24 from a roll 25, is positioned on a foraminous screen 20 upstream from the fluff preparation zone 14. As facing sheet 24 passes through the fluff preparation zone, the core forming fibers are deposited on the facing sheet to the desired depth as established in a conventional manner, such as by use of a doctor roll. The unfused core forming fibers, indicated at 28 in FIG. 1, together with the facing sheet 24, are carried by the belt 20 into a thermobonder 22. The thermobonder 22 heats the fibers to a temperature above the melting point of at least one thermoplastic fiber material in the core. For example, the melting point of some types of polyethylene pulp is 122° to 134° C., the melting point of some types of polypropylene fiber is 160° to 165° C., and the softening point of some types of polyester fibers, such as Kodel® is over a broad range, but may be bonded, for example, at about 170° C. These fibers are selected to resist damaging bleach and detergents and which melt at a temperature above which the towels are to be subjected in a dryer. This heat fuses the core and also bonds the core to the facing sheet. Although calendars, infrared heaters, and other heating devices may be employed to heat fuse the core, the illustrated thermobonder 22 comprises a flow-through dryer. The exact heating conditions, which can be readily ascertained by one skilled in the art, must be determined for the specific fiber blend being used. The time that the core spends within the thermobonder 22 is also readily ascertainable by one skilled in the art. Generally this time ranges from about one hundred milliseconds to one minute depending in part upon the temperature of the thermobonder and the line speed at which the screen is traveling. Adhesive bonding or other bonding approaches may also be used. Thereafter, the core can then be densified at eventual edge margin sections of an article to be formed from the core and otherwise processed as explained below.

Although not required, the thermobonder has three stages 30, 32 and 34. In each stage, heated air enters from a respective inlet 36, 38 and 40. The entering heated air passes successively through the core forming fibers 28, the facing sheet 24, the belt 20 and to a respective exit outlet 42, 44 and 46. A pressure differential is maintained across the traveling materials to draw the heated gas through these materials. For example, the inlets may be pressurized relative to the outlets or a vacuum may be applied to the outlets. The melted thermoplastic material fibers of the core 28 fuse or thermobond the core to itself and also to the fact sheet 24. The temperature is such that the face sheet 24 is not melted by the thermobonder 22.

Typical line speeds for the screen 20 are from 100 to 250 feet per minute with 150 feet per minute being a normal operating speed. The thermobonder 22 includes an optional convention oven or apron 50. This oven maintains the temperature of the bonded core and facing as these materials travel toward a feature forming zone 54.

The upper cover sheet 56, which may be identical to the sheet 24, is fed from a roll 58 to the exposed surface 60 of the core. The sheet 56 may instead be placed on top of the core and fed through the thermobonder so as to be bonded to the core as the core is thermobonded.

At feature forming zone 54, the multilayered or composite web is typically bonded or densified along at least a section of the eventual peripheral edge margin of an article to be formed. Typically, the entire eventual peripheral edge margin of the article is densified. In addition, field bonds are also formed within the eventual field of the article intermediate the peripheral edge margin. These densified low wicking rate bonded areas increase the ability of the towels to hold up during laundering. A number of suitable processes may be used to form these densified areas. These include ultrasonic bonding and adhesive bonding. However, the preferred approach is to emboss these bond areas. To this end, opposed sets of embossing rolls 70, 72 and 74, 76 are positioned as shown. The illustrated roll 70 comprises a field bond feature forming roll having a projecting pattern of field bond forming contacts 80 which press against the face sheet and other layers of the composite material. Roll 72 may comprise a roll with field bond forming contacts, but typically comprises a smooth surfaced anvil roll which is positioned against the top sheet 56. Typically another pair of rolls (not shown) like rolls 70, 72 are used to emboss the top sheet 56 with the feature forming roll located adjacent to and above the sheet 56 and the anvil roll located below the sheet 24. Similarly, roll 74 comprises a peripheral edge margin feature forming roll having contacts 82 arranged to define those sections of the eventual peripheral edge margins of the article which are to be densified. Normally, the entire eventual edge margin of the article is densified by feature forming roll 74. Roll 76 comprises a smooth anvil roll which backs up the feature forming roll.

A conventional temperature control 90, 92, 94 and 96 is provided for each of the respective rolls 70, 72, 74 and 76 for independently controlling the temperature for these rolls (and for other rolls) is used. If the same materials are being used for the backing and facing sheets, typically these rolls are kept at the same temperature. The rolls are typically held at temperatures below the melting point of the core fibers, for example, at 120°-130° C, depending upon the materials. In cases where the top sheet 56 has a relatively low melting point, rolls 72 and 76 may be kept somewhat cooler (i.e. at 80°-110° C. depending upon the material) than rolls 70 and 74 to act as a heat sink to assist in cooling the backing sheet 56 below its melting point.

The temperature of the embossing rolls 70 through 76 is preferably held cooler than the melting point temperatures of both the core 28 and the face sheet 24. By maintaining the core 28 above its thermobonding temperature when it reaches the embossing rolls, the feature forming rolls bring the core temperature below the thermobonding temperature to thermoset or heat seal and compress the peripheral edge margins and field bonds in the pad or other article. Also, the core 28 and cover sheet 24 do not tend to delaminate when embossed with these cooler embossing rolls. The field bond contacts 80 and peripheral margin bond contacts 82 may also be placed on the same roll.

The nip gap between the contacts 80 and the corresponding anvil roll is typically from about zero to twelve thousandths of an inch with zero to three thousandths of an inch being preferred. Typically one-quarter inch to one-half inch spacing is provided between the contact and the relief portions of these rolls. Embossing pressures are variable, depending upon the desired density of the bonded areas, with 1,000 psi to 5,000 psi embossing pressures being typical.

The field embossed patterns typically comprise spaced apart embossed areas such as dots, intersecting lines or elongated bars. Preferably, for towels of the present invention, about 3% to 20%, and most preferably about 7% to 8% of the surface of the article is embossed with field patterns. However, for some applications, lesser or greater amounts of embossing may be provided.

Also, a pattern of contacts in the form that would be left by the raised areas of a screen have proven particularly suitable. FIGS. 4 and 4a (the latter figure being close to actual size) illustrate contacts 80 of an embossing roll that provide such an embossing pattern. These contacts leave a pattern of bond areas which are elongated with adjacent bond areas being approximately one-fourth of an inch apart and with their axes oriented ninety degrees relative to one another. The individual embossed areas are typically about three millimeters long and one millimeter wide. The unembossed, but bonded (thermobonded, adhesive bonded or otherwise bonded) areas between the densified areas in effect comprise absorbent pockets for use in holding liquid during use of the towel.

It has also been found that the "wipe dry" characteristics of a covering or towel wiping surface can be varied by controlling the percentage of the surface area which is embossed. In testing performed as of this time, the "wipe dry" properties of the wiping surface of the towel is improved by increasing the spacing between the embossed area. Also, by decreasing the spacing between embossed areas, a coarser surface results and enhances the use of the surface in scrubbing a surface.

For purposes of this description, the term "wipe dry" refers to the percentage increase in the weight (wet-only weight/dry weight)×100]of a 3 inch by 31/2 inch sample of material, pressed against a nonabsorbent surface by a weight of 200.15 gm, and drawn at a constant speed of 50 inches per minute, a distance of 14 inches through a puddle of 10 ml of deionized water on the surface. The water is located 5 inches from the sample at the time the motion is started. In this test, 21/2"×2 1/2" inch section of the material is held by the weight against the surface and the leading and side edges of the sample are not immersed in the liquid. The leading edge in this context refers to the edge which leads in the direction of travel of the weight during the test.

Typical "wipe dry" characteristics of towels manufactured in accordance with the present invention range from about 300 to about 800 percent and are preferably about 300-500 percent. Also, different embossing patterns can be used on the respective cover surfaces. For example, a towel can be produced with a first surface with a "wipe dry" characteristic for use in more difficult scrubbing of a surface and for mopping up relatively large amounts of water. At the same time, the other surface can be provided with a smoother texture and higher "wipe dry" characteristics for final drying or wiping operations.

The direction tensile strength of articles formed in this manner is enhanced by the embossed areas and by the thermobonded core. In addition, by embossing all or sections of the eventual peripheral edge margins of the article, the tensile strength of the article in X, Y and Z directions is substantially improved, especially at the edge. In addition, a densified peripheral edge margin impedes the leakage of liquid from the towel through the edge.

To provide a towel which is durable so as to withstand at least about five wash and dry cycles on average, the dry Z direction tensile strength of the composite towel, including a cover sheet or sheets and the core should be no less than about five to six kPa. The Z direction tensile strength may be determined by taking a 2"×2" sample of material, mounting the sample by adhesive to plates and then measuring the force required to pull the sample apart in the Z direction. In addition, to provide a durable towel, the composite towel should have a dry tensile index in the machine direction which is preferably greater than or equal to five and a dry tensile index in the cross machine direction which is greater or equal to about three. In determining the tensile index, one inch wide samples of the composite towel may be positioned with one edge in a clamp and the opposed edge pulled until failure occurs. The tensile index is a ratio of the force required to cause failure to the basis weight of the material and may be expressed in Nm/g. A towel with the above strength values and with the limited stretch cover sheets has proven to be launderable in excess of five times. The above strengths which result in a durable towel represents the dry strength of the towel.

Following embossing, the articles may be separated from the composite material. Although the articles can be die cut or otherwise separated in the manufacturing line following embossing, in the illustrated approach the articles are separated from the composite materials at a cutting location separate from the line. A laser, die, waterknife or other cutting mechanism 100 is used to separate the composite materials into pads 102 which contain the articles defined by the peripheral edge margins embossed thereon. Plural relief areas, for example 84, 86, are defined by the roll 74 such that the roll can be used to form plural towels from the composite web. The separate pads 102 are then stacked in a bin 104 for subsequent transportation to a cutting zone where the finished articles are severed from the pads.

Optional pin register defining contacts (not shown) may be included on feature roll 74. These contacts form corresponding bonds on the individual pads 102. These latter bonds may be registered with pin 110 of bin 104 so that the individual pads 102 are aligned in the bin. More than one of the aligned pads can then be cut at a time at the cutting location with the pads being held in position by pins inserted through the bonds defined by contacts 108. Other pad alignment mechanisms can also be used. Also, individual pads may be cut rather than cutting the pads in stacks.

Adhesive applicators, such as shown in dashed lines at 114 in FIG. 1., may be used to apply an adhesive coating to the surface 60 of the core or directly to the backing sheet 56 to secure the sheet 56 to the core. A similar adhesive applicator may be used to apply adhesive to secure the face sheet to the core if the face sheet 24 is secured other than by passing the face sheet through the thermobonder or embossing rolls. For enhanced durability and ease of manufacturing, thermobonding of both cover sheets to the core, followed by embossing, is preferable. Although the cover sheets 24, 56 may be secured solely by embossing and without thermobonding, this reduces the durability of the resulting towels.

A wide variety of adhesive binders can be used for this purpose. For example, thermoplastic resin adhesives and aqueous latexes are suitable. Ethylene/vinyl/acetate copolymer is one form of suitable adhesive binder. In addition, pressure sensitive adhesives are also suitable.

The desired articles are cut from the pad sections 102 by a cutting mechanism such as a die, laser, or water knife. A suitable water knife cutting system is shown schematically in FIG. 3. Devices using a water knife, sometimes called a fluid jet, for cutting strip-like material are known. U.S. Pat. No. 4,620,466 of Jumel et al. describes one such device. Similarly, a water knife may be used in conjunction with a cutting system sold under the brand name GerberCutter by Gerber Garment Technology, Inc. of South Windsor, Connecticut.

With reference to FIG. 3, a water knife 140 is supported by a computer controlled movable support, such as found in the GerberCutter apparatus or the cutting machine of the aforementioned Jumel et al. patent. One or more pad sections 102 to be cut are positioned on a table 144. The table is capable of moving the pads in a direction perpendicular to the direction that the water knife is moved by support 142. This combination of motion, as described in the Jumel et al. patent and in the analogous GerberCutter system, allows any arbitrary shaped article to be cut from the pad sections 102. A water stream 146 from water jet 140 severs the articles. To stop a particular cut, the water jet stream 146 is deflected by air, to a position shown in dashed lines at 146' and to a drainage trough 172. Air for deflecting the water knife is provided by a source 174 through a valve 176 and to an air nozzle 178. The valve 176 is controlled by a control circuit 180 to open and close the valve as required. The position of the cut may be controlled to be within the densified edge margin of the article, or just outside of the densified edge margin, or a combination thereof. If the article is severed from the pad outside of the densified edge margin, a softer edge is produced.

FIG. 5 illustrates one example of a towel 183 of the present invention manufactured as described above. Only a portion of the towel is shown with a surface texture of the type resulting from embossing the towel with a screen or embossing rolls having a pattern of embossing contacts such as 80 in FIG. 4. The cover stock shown in the FIG. 5 illustration is apertured as indicated by the small apertures 184 in this figure. The deeper embossed areas formed by the embossing contacts 186 are indicated at 186.

The manufacture of several exemplary towels in accordance with the present invention is described below with the various characteristics and properties being indicated.

One specific exemplary towel had a core comprised of 20% by weight Kodel® 410 fibers and 80% by weight wood pulp fibers. The specific wood pulp fibers utilized in this example were in NB-316 fibers available from Weyerhaeuser Company. These fibers were mixed and thermobonded using Sontara® 8010 cover layers at opposite sides of the core. The core had a basis weight of 100 g/m². In addition, the basis weight of this specific Sontara® material was 1.3 ounces per yd². The top surface was positioned adjacent to a 1/8th inch mesh screen while the bottom surface was positioned adjacent to a 1/4 inch mesh screen. The sandwich of materials was pressed at 600 psi at 320° F. for 2 minutes.

The following properties were observed. For comparison purposes, the corresponding properties of a 100% cotton bar towel are also listed.

    ______________________________________                                         Characteristic   Example Towel Bar Towel                                       ______________________________________                                         Basis Weight (g/m.sup.2)                                                                        219           293                                             Density (g/cm.sup.3)                                                                            0.127         0.175                                           Bulk dry (cm.sup.3 /gm)                                                                         7.88          5.72                                            Bulk wet (cm.sup.3 /gm)                                                                         1.34          1.53                                            Demand Absorbency (ml/gm)                                                                       3.65          ****                                            Liquid Migration rate                                                                           180           232                                             (cm.sup.2)                                                                     Machine direction tensile                                                                       24.5          18.1                                            strength dry (Nm/gm)                                                           Cross machine direction                                                                         6.32          15.8                                            tensile strength dry                                                           (Nm/gm)                                                                        Machine direction tensile                                                                       25.4          21.7                                            strength wet (Nm/gm)                                                           Cross machine direction                                                                         6.85          18.8                                            wet (Nm/gm)                                                                    Z direction tensile strength                                                                    29.8          94.6                                            dry (kN/m.sup.2)                                                               Wicking-machine direction                                                                       11.3          6.91                                            Wicking-cross machine                                                                           13.9          6.85                                            direction                                                                      Handle (gm)      81            4.36                                            Wipe dry top surface (%)                                                                        363           434                                             Wipe dry bottom surface (%)                                                                     433           424                                             ______________________________________                                    

In the above examples, the basis weight can be determined using Tappi T-410 OM method (Tappi being the Technical Association of Pulp and Paper Industry); the density can be determined using Tappi T-410 OM; the bulk was determined using Tappi T-426 WD; the cross machine and machine direction tensile strength can be determined using Tappi T-494; the Z direction tensile strength can determined using Tappi T-506; the handle can be determined using Tappi T-498 SU-66; the demand absorbency can be determined using ASTM-D535 (ASTM referring to the American Society of Testing Materials); and the liquid wicking rate can be determined using Tappi T-451 (UM451). The liquid migration rate was determined by pouring 10 ml of liquid onto the center of a 40 cm×40 cm sample. After two minutes, the length and width of spreading of the liquid was measured and the area to which the liquid spread was determined to be the migration area. The liquid wicking rate can be determined using Tappi T-451 (UM451). As can be seen from the above example, the use of a 1/8th inch mesh screen against one of the wiping surfaces (the top surface) and a 1/4 inch screen against the other of the wiping surfaces (the bottom surface) produces a towel with differing wipe dry characteristics. That is, the wipe dry characteristics of the bottom surface were higher than the wipe dry characteristics of the top surface. In some other tests, when the same size mesh screens were used at each side of a towel, the wipe dry characteristics were approximately the same at each of the towel surfaces. Thus, by controlling the embossed area of the particular surfaces, the wipe dry characteristics can be controlled to vary these characteristics, or maintain them approximately equal.

Towels produced in accordance with the above example held up during laundering repeated times. For example, on average, these towels could be machine washed and dried five or more times while still maintaining their desired characteristics.

For comparison purposes, towels made in accordance with the present invention are compared with towels made in accordance with example 12 of U.S. Pat. No. 4,886,697. Specifically, in a first case, labeled example A in the table below, a towel was manufactured in accordance with the teachings of example 12 of the Perdelwitz, Jr., et al. patent. This towel was formed with a core of twenty percent Pulpex® and eighty percent wood pulp fibers with nonwoven covering sheets, namely APN 185 carded thermobonded nonwoven polypropylene sheets (the APN 185 cover sheets referred to in the Perdelwitz, Jr. et al. patent being unavailable). The facing and backing sheets were thermobonded to the core and heat sealed at the edges. Field bonds comprising dots spaced about two inches apart were also provided as specified in this example 12.

Example B was prepared in the same manner as example A except that an embossing pattern was used to form field bonds which are the same as shown in FIG. 5 of the present patent application. In this case, approximately 7.9 percent of the surface area of the towel was bonded by these field bonds.

In the third example, example C, a towel was prepared in the same manner as examples A and B, with a number of exceptions. First, the core was formed of eighty percent wood pulp and twenty percent Kodel® 410 polyester fibers. In addition, instead of the APN 258 cover stock, a cover stock from of fifty percent rayon and fifty percent polyester fibers was used. This cover stock was prestretched and heat set. Before stretching, the cover stock was capable of elongating 134 percent in the cross machine direction and 42.6 percent in the machine direction. Following prestretching and setting, the cover stock was capable of elongating sixty percent in the cross machine direction and forty percent in the machine direction. Prestretching and setting was accomplished by stretching the material in the cross machine direction approximately forty-five percent, heating the stretched material to 200° C., and cooling the stretched material to set the material. In example C, the handle was 31.5. For towels used for scrubbing purposes a higher handle, such as about 100, would be desirable. A lower handle, for example, a handle of 20, would be more conformable and drapable. Within this handle range of 20 to 100, excellent towels for food service purposes are provided if the handle is about 20 to 40.

In the fourth example, example D, the core was formed of twenty percent Kodel®, seventy percent wood pulp, and ten percent high melt temperature polyester reinforcing fibers of one-half inch in length. These reinforcing fibers are long enough to span the distance between the embossed areas of the towel. These polyester reinforcing fibers have a melt temperature of about 220° to 260° C. and therefore remained intact because thermobonding was performed at about 170° C.

A number of towels made in this manner were then subjected to laundering involving both a wash and a dry cycle. A Sears Kenmore-80 clothes washer was used for the wash cycle. The clothes washer was set on a normal cycle with a ten minute was time and a medium water level. One-half cup of Arm & Hammer heavy duty detergent was used during washing. The towels were washed with three to four dish towels and one tablecloth to simulate the normal impact that occurs between items in a load being washed. The total wash cycle, including rinsing and spin dry time was twenty five minutes. The drying cycle was accomplished in a Sears Kenmore dryer without other items present in the dryer. The dryer was set on a permanent press setting for five to eight minutes.

Table I below summarizes the tensile strength comparisons of the various examples dry and wet, prior to washing, and following one was cycle.

                  TABLE I                                                          ______________________________________                                                Prior to Washing                                                                             Following One Washing                                            Tensile Index                                                                            Z-Tensile                                                                              Tensile Index                                                                              Z-Tensile                                        MD   CD      KPa      MD   CD    KPa                                    ______________________________________                                         Example A                                                                      Dry      6.4    0.8     1.4    6.6  0.8   1.6                                  Wet      6.4    0.8     1.3    6.4  0.8   1.3                                  Example B                                                                      Dry      7.6    1.4     4.7    6.1  0.9   3.7                                  Wet      7.1    1.0     3.4    5.7  0.8   2.7                                  Example C                                                                      Dry      13.5   5.6     29.2   10.7 3.6   11.6                                 Wet      11.7   4.1     12.8                                                   Example D                                                                      Dry      17.9   9.9     31.3   12.8 5.1   17.1                                 Wet      12.3   4.3     6.9                                                    ______________________________________                                    

As a result of these tests, the example A towel disintegrated following one laundering cycle. That is, the densified edge of this towel and cover sheets remained, but substantially all of the core portion of the towel fell apart and balled up within the cover sheets. The towel of example B disintegrated after three laundering cycles. In comparison, the towels of examples C and D each lasted for more than ten laundering cycles. Thus, although towels produced in accordance with example 12 of the aforementioned Perdelwitz, Jr., et al. patent are very useful, they are not durable in the sense that they did not survive five or more laundering cycles. By comparison, the towels of the present invention survived well in excess of five laundering cycles and thus are durable.

Having illustrated and described the principles of our invention with reference to several preferred embodiments, it should be apparent to those of ordinary skill in the art that such embodiments may be modified in detail without departing from such principles. We claim as our invention all such modifications as come within the true spirit and scope of the following claims. 

We claim:
 1. A durable towel comprising:an absorbent core comprising a mixture of plural types of fibers, at least one of the fibers being heat bondable, the core being heat bonded and having a basis weight of from about fifty to one hundred and fifty g/m², the heat bondable fibers of the core being present in an amount of from about 15% to 40% of the total dry weight of the core; the towel including at least one cover sheet secured to the core, the cover sheet being stretchable no more than eighty percent of its length; the towel having densified bond areas at its interior, the densified bond areas occupying from about 3% to about 20% of the surface of that towel; and the towel on average being launderable at least five times without tearing or separation of the core and cover sheet.
 2. A towel according to claim 1 having two cover sheets with the core positioned therebetween, the cover sheets being of an apertured nonwoven heat bondable material and being embossed with an embossing pattern at the interior portions of the towel.
 3. A towel according to claim 2 in which the cover sheets are stretchable no more than about sixty to seventy percent.
 4. A towel according to claim 2 in which the cover sheets are prestretched and heat set prior to inclusion in the towel so as to limit their stretchability.
 5. A towel according to claim 3 in which the cover sheets are prestretched and heat set prior to inclusion in the towel so as to limit their stretchability.
 6. A towel according to claim 1 having densified edges so as to form a substantial liquid barrier at the edges.
 7. A towel according to claim 2 in which the cover sheets have a machine and cross machine direction grab tensile strength of at least three kilograms, the towel having a tensile Z direction dry strength of at least about five to six kPa, a machine direction dry tensile index of at least five and a cross machine direction dry tensile index of at least about three.
 8. A towel according to claim 1 with first and second side surfaces, the towel being embossed with a first pattern on one surface thereof and with a second embossed pattern on the other side surface thereof, the second embossed pattern differing from the first embossed pattern so as to provide differing wipe dry characteristics at the first and second surfaces of the towel.
 9. A towel according to claim 8 in which the first embossed pattern is formed by contact surfaces like those of a one-quarter-inch mesh screen and the second embossed pattern is formed by contact surfaces like those of a one-eighth-inch mesh screen.
 10. A towel according to claim 7 having a handle of from 20 to 100 grams.
 11. A towel according to claim 7 having a handle of about 20 to 40 grams.
 12. A towel according to claim 2 including fibers of a length which is sufficient to span the distance between the interior densified bond areas and which have a melt temperature which is above the heat bonding temperature.
 13. A durable towel comprising:an absorbent core comprising a mixture of plural types of fibers, at least one of the fibers being heat bondable, the core being heat bonded and having a basis weight of from about fifty to one hundred and fifty g/m², the heat bondable fibers of the core being present in an amount of from about 15% to 40% of the total dry weight of the core; the towel including at least one cover sheet secured to the core in which the cover sheets are prestretched and heat set prior to inclusion in the towel so as to limit their stretchability; the towel having densified bond areas at its interior, the densified bond areas occupying from about 3% to about 20% of the surface of the towel; and the towel on average being launderable at least five times without tearing or separation of the core and cover sheet. 